Influence of nickel and copper on liquid structure of CuAlNi shape memory alloys

Influence of nickel and copper on liquid structure of CuAINi shape memory alloys

Liquid structure of molten pure Cu, Cu-12Al, Cu-12Al-4Ni (mass fraction, %) alloys has been investigated using the X-ray diffraction method. It is found that the main peak of the structure factor of pure Cu is symmetrical. In the front of main peak, the curve takes on a shape of parabola, whereas a distinct pre-peak has been found around a scattering vector magnitude of 18.5 nm-1 in the structure factor of the liquid Cu-12Al alloy. This pre-peak increases its inten-sity with the addition of Ni in the liquid Cu-12Al-4Ni alloy. The appearance of a pre-peak is a mark of the mediate-range order. Based on Daken-Gurry theory and according to mu-tual interaction between unlike atoms, the analysis of corre-lation between different composition and liquid structure was done: the strong interaction exists between Cu and Ni, so Cu-Al can form strong chemical bond which causes compound-forming behavior. Therefore, the medium-range size clusters can form in melt. The presence of the pre-peak corresponds to these

Liquid structure of molten pure Cu, Cu-12Al, Cu-12Al-4Ni (mass fraction, %) alloys has been investigated using the X-ray diffraction method. It is found that the main peak of the structure factor of pure Cu is symmetrical. In the front of main peak, the curve takes on a shape of parabola, whereas a distinct pre-peak has been found around a scattering vector magnitude of 18.5 nm-1 in the structure factor of the liquid Cu-12Al alloy. This pre-peak increases its inten-sity with the addition of Ni in the liquid Cu-12Al-4Ni alloy. The appearance of a pre-peak is a mark of the mediate-range order. Based on Daken-Gurry theory and according to mu-tual interaction between unlike atoms, the analysis of corre-lation between different composition and liquid structure was done: the strong interaction exists between Cu and Ni, so Cu-Al can form strong chemical bond which causes compound-forming behavior. Therefore, the medium-range size clusters can form in melt. The presence of the pre-peak corresponds to these clusters. The addition of Ni can strengthen the interaction between unlike atoms and increase the sizes of clusters, thus result in the height of pre-peak increasing.