Poly (L-lactide) was prepared by bulk polymerization ofL-lactide at 140°C in the presence of stannous octoate. The polymer products were characterized by number average molecular weight Mn, weight average molecular weight Mw and molecular weight distribution MWD (M w/M n) respectively. The results showed that stannous octoate was a high effective catalyst, and coordinated insertion mechanism of the reaction was proposed.
Poly (L-lactide) was prepared by bulk polymerization ofL-lactide at 140°C in the presence of stannous octoate. The polymer products were characterized by number average molecular weight Mn, weight average molecular weight Mw and molecular weight distribution MWD (M w/M n) respectively. The results showed that stannous octoate was a high effective catalyst, and coordinated insertion mechanism of the reaction was proposed.
作者
Chen Lian xi 1, Wang Jun 2, Fu Jie 2, Lei Jia heng 1 1. School of Natural Sciences, Wuhan University of Technology, Wuhan 430070, Hubei, China 2. School of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, Hubei, China
基金
SupportedbythekeyProjectoftheMinistryofScienceandTechnology ( 96-920-2 1)