Laser surface alloying of γ TiAl alloy with nitrogen was studied under the constant protective nitrogen current (20l /min). The experimental results shown that the surface multi layers formed with experimental parameters could be up to 600μm depth; it consists of TiN,Ti 2AlN,α 2 and γ phases, without AlN, and the irregular coarse continuous “flow” line,dendrite,needle and granular nitrides disperse on the fine dendrite casting α 2 and γ phases substrate. The microstructure and compositions in the nitiding layer were determined and analyzed by SEM and EPMA and the mechanism for the formation of microstructure in the nitriding layer was also discussed.
Laser surface alloying of γ TiAl alloy with nitrogen was studied under the constant protective nitrogen current (20l /min). The experimental results shown that the surface multi layers formed with experimental parameters could be up to 600μm depth; it consists of TiN,Ti 2AlN,α 2 and γ phases, without AlN, and the irregular coarse continuous “flow” line,dendrite,needle and granular nitrides disperse on the fine dendrite casting α 2 and γ phases substrate. The microstructure and compositions in the nitiding layer were determined and analyzed by SEM and EPMA and the mechanism for the formation of microstructure in the nitriding layer was also discussed.