摘要
A stable colloidal boehmite sol was made with the aluminium iso propoxide made in China and used to prepare the supported γ alumina membrane using sol gel method. The γ alumina thin layer was characterized by SEM, N 2 sorption method and permeation measurement. The γ alumina membrane was prepared with uniform surface, thickness of 3 μm and average diameter of about 5 nm. The permeabilities of the single gases of H 2, N 2, Ar and their separation factors were measured. The experimental data explained a behavior of Knudsen diffusion for the gas transport through the thin membrane.
A stable colloidal boehmite sol was made with the aluminium iso propoxide made in China and used to prepare the supported γ alumina membrane using sol gel method. The γ alumina thin layer was characterized by SEM, N 2 sorption method and permeation measurement. The γ alumina membrane was prepared with uniform surface, thickness of 3 μm and average diameter of about 5 nm. The permeabilities of the single gases of H 2, N 2, Ar and their separation factors were measured. The experimental data explained a behavior of Knudsen diffusion for the gas transport through the thin membrane.