Secondary M23C6 precipitation around primary MC carbide in a directionally solidified cobalt-base saperalloy was investigated duriny aging at 850℃. The results show that it was closely related to the decomposition of the MC. Two mechanisms were suggested,i.e. the in situ reaction, MC+γ→M23C6+C, and the direct reaction, M+C→M23C6,in which MC acted as a carbon source.
Secondary M23C6 precipitation around primary MC carbide in a directionally solidified cobalt-base saperalloy was investigated duriny aging at 850℃. The results show that it was closely related to the decomposition of the MC. Two mechanisms were suggested,i.e. the in situ reaction, MC+γ→M23C6+C, and the direct reaction, M+C→M23C6,in which MC acted as a carbon source.