摘要
This paper examines the effects of shrink - resist treatment, washing cycle and fabric tightness on the shrinkage properties of plain knitted fabrics made from 100% wool, acrylic/wool (50/50) and acrylic/wool (70/30). It was found that shrinkages of both treated and untreated wool fabrics were negatively correlated to fabric tightness and exceeded the IWS shrinkage limits (5% in length and 8 % in area) after 2 - 5A washing cycle. The effect of tightness was not as obvious with acrylic/wool (A/W) fabrics, but the shrinkage was seen to increase with stages of washing cycle for untreated A/W fabrics with some exceeding IWS standard. By applying the DC 109 shrink - resist solvent treatment, it was identified that by with higher percentage of acrylic fibre blended with wool, shrinkage could be reduced considerably and within acceptable limits.
This paper examines the effects of shrink - resist treatment, washing cycle and fabric tightness on the shrinkage properties of plain knitted fabrics made from 100% wool, acrylic/wool (50/50) and acrylic/wool (70/30). It was found that shrinkages of both treated and untreated wool fabrics were negatively correlated to fabric tightness and exceeded the IWS shrinkage limits (5% in length and 8 % in area) after 2 - 5A washing cycle. The effect of tightness was not as obvious with acrylic/wool (A/W) fabrics, but the shrinkage was seen to increase with stages of washing cycle for untreated A/W fabrics with some exceeding IWS standard. By applying the DC 109 shrink - resist solvent treatment, it was identified that by with higher percentage of acrylic fibre blended with wool, shrinkage could be reduced considerably and within acceptable limits.