摘要
The single phase La1-x NaxCu2O4 crystals were synthesized by an electrochemical method from molten KOH/NaOH/KNO3 at 280-300℃ while La2-yNayCuO4 were prepared by precipitation from the same molten salt. The resulting crystals were characterized by using SEM, XRD, EDX and XPS. XPS analysis revealed that the La3d satellite structures of La1-xNaxCu2O4 were quite different from those of La2-yNayCuO4. These differences have been attributed to the changes in crystal structures, bond lengths and covalent character of the metal-ligand bonds.
The single phase La1-x NaxCu2O4 crystals were synthesized by an electrochemical method from molten KOH/NaOH/KNO3 at 280-300℃ while La2-yNayCuO4 were prepared by precipitation from the same molten salt. The resulting crystals were characterized by using SEM, XRD, EDX and XPS. XPS analysis revealed that the La3d satellite structures of La1-xNaxCu2O4 were quite different from those of La2-yNayCuO4. These differences have been attributed to the changes in crystal structures, bond lengths and covalent character of the metal-ligand bonds.
基金
Project supported by the National Natural Science Foundation of China (No. 29573143) and the National Center of Research and Development on Superconductivity of China