The synthetical soft magnetic properties were reported for newly-developed nanocrystalline Fe73.5Cu1Nb0.9 Mo2.1Si13.5B9 and Fe73.5Cu1Nb0.5 Mo2.5Si13.5B9 alloys. The levels of high-frequency losses of the new alloys are P3/100k=612 and 670 kWm-3, P2/200k=880 and 973kWm-3, P2/500k=4300 and 4600 kWm-3, P0.5/1000k=860 and 920 kWm-3, respectively. They are significantly lower than those of the superior power Mn-Zn ferrite H7c4. The dependence of core loss on frequency and amplitude flux density has been analyzed. The practical applications of the new alloys to switching mode power supplies with the output power of 1 and 2kW were reported.
The synthetical soft magnetic properties were reported for newly-developed nanocrystalline Fe73.5Cu1Nb0.9 Mo2.1Si13.5B9 and Fe73.5Cu1Nb0.5 Mo2.5Si13.5B9 alloys. The levels of high-frequency losses of the new alloys are P3/100k=612 and 670 kWm-3, P2/200k=880 and 973kWm-3, P2/500k=4300 and 4600 kWm-3, P0.5/1000k=860 and 920 kWm-3, respectively. They are significantly lower than those of the superior power Mn-Zn ferrite H7c4. The dependence of core loss on frequency and amplitude flux density has been analyzed. The practical applications of the new alloys to switching mode power supplies with the output power of 1 and 2kW were reported.