Geometrical Close Packed(GCP) phase in Fe-Cr-Ni alloy was quantitatively isolated and precisely determined when electrolyzed in 10%H_3PO_4 electrolyte at a low current density of5 mA/cm^2 and 22 ℃±1 ℃.The transpassive dissolution potential of the alloy matrix under above conditions is about 1 140 mV(SCE),at which GCP phase is in passive state and can be isolated from the alloy.
Geometrical Close Packed (GCP) phase in Fe Cr Ni alloy was quantitatively isolated and precisely determined when electrolyzed in 10 % H 3PO 4 electrolyte at a low current density of 5 mA/cm 2 and 22 ℃±1 ℃. The transpassive dissolution potential of the alloy matrix under above conditions is about 1 140 mV (SCE), at which GCP phase is in passive state and can be isolated from the alloy.[WT5”HZ〗