Investigations have been made on the effects of temperature and fine disperse phase of disordered γ on strain hardening rate of Ni3Al based alloy. The result is found that there exists a peak temperature for the strain hardening rate of Ni3Al based alloy below the peak temperature of its yield strength. Analysis shows that the appearance of the peak temperature of strain hardening rate is caused by both the decreasing of the movability of <101> superdislocations on {111}slip plane and the increasing of the dynamic recovery in Ni3Al with increasing temperature. A Ni3Al based alloy hardened by disperse phase of disordered γ has been obtained by controlling chemical composition and treating processes. The peak temperature of strain hardening rate of this alloy is increased due to the fine disperse phase of disordered γ, which causes the reductions of the movability of the superdislocations and the dynamic recovery in Ni3Al
Investigations have been made on the effects of temperature and fine disperse phase of disordered γ on strain hardening rate of Ni3Al based alloy. The result is found that there exists a peak temperature for the strain hardening rate of Ni3Al based alloy below the peak temperature of its yield strength. Analysis shows that the appearance of the peak temperature of strain hardening rate is caused by both the decreasing of the movability of <101> superdislocations on {111}slip plane and the increasing of the dynamic recovery in Ni3Al with increasing temperature. A Ni3Al based alloy hardened by disperse phase of disordered γ has been obtained by controlling chemical composition and treating processes. The peak temperature of strain hardening rate of this alloy is increased due to the fine disperse phase of disordered γ, which causes the reductions of the movability of the superdislocations and the dynamic recovery in Ni3Al