In this paper, two types of high loft nonwoven fabrics have been constructed in the laboratory apparatus made by ourselves with different binders (polyamide and polyethylene powder) and varying binder contents (10%, 20%, 30% and 40%). The tensile and compression properties of these nonwoven fabrics were tested. It was found that one can reduce powder binder content to increase loft and softness of nonwoven fabrics, but it has to sacrifice its tensile strength. Adhesion force between binder and single fibre was also explored. The experiments showed that the adhesion force at the interface between binder and fibre depends on the fibre variety, the fibre surface morphology, heating temperature and heating time etc..
In this paper, two types of high loft nonwoven fabrics have been constructed in the laboratory apparatus made by ourselves with different binders (polyamide and polyethylene powder) and varying binder contents (10%, 20%, 30% and 40%). The tensile and compression properties of these nonwoven fabrics were tested. It was found that one can reduce powder binder content to increase loft and softness of nonwoven fabrics, but it has to sacrifice its tensile strength. Adhesion force between binder and single fibre was also explored. The experiments showed that the adhesion force at the interface between binder and fibre depends on the fibre variety, the fibre surface morphology, heating temperature and heating time etc.
基金
高等学校博士学科点专项科研基金资助项目论文