摘要
The γ induced polymerization of styrene in the presence of polar additives such as tributylphosphate, triethyl amine and ethanol was studied at dose rate of 5.0×10^(17) eV/ml. min. The re-sult shows that radiation induced polymerization of styrene was sensitized by the three kinds ofadditives at the approximate same rate and the experimental results were in agreement with thetheoretical calculation of WAS equation. The cause of sensitization is due to the proton transfer.
The γ induced polymerization of styrene in the presence of polar additives such as tributylphosphate, triethyl amine and ethanol was studied at dose rate of 5.0×10^(17) eV/ml. min. The re-sult shows that radiation induced polymerization of styrene was sensitized by the three kinds ofadditives at the approximate same rate and the experimental results were in agreement with thetheoretical calculation of WAS equation. The cause of sensitization is due to the proton transfer.