摘要
The serratedflow of alloy LC9 with different regimes of heat treatment has been investigated at constant rate of stretching.The critieal strain ε_c at the starting of serrated flow increases with the extension of aging.The activation energy of the process is 0.63 e V which is consistent with the diffusion activation energy of vacancies in A1.The ε_c decreases while the strain rate ε increases,i.e.,with negative strain rate relation.This relation is contrary to that of the an- nealed samples.It shows that the serrated 17ow of annealed sample is controlled by deformation vaeancies,and that of aged sample is controlled by quenching vacancies.The den- sity and shape of the serration are changed by aging.The mechanism of the above mentioned results is discussed.
The serratedflow of alloy LC9 with different regimes of heat treatment has been investigated at constant rate of stretching.The critieal strain ε_c at the starting of serrated flow increases with the extension of aging.The activation energy of the process is 0.63 e V which is consistent with the diffusion activation energy of vacancies in A1.The ε_c decreases while the strain rate ε increases,i.e.,with negative strain rate relation.This relation is contrary to that of the an- nealed samples.It shows that the serrated 17ow of annealed sample is controlled by deformation vaeancies,and that of aged sample is controlled by quenching vacancies.The den- sity and shape of the serration are changed by aging.The mechanism of the above mentioned results is discussed.