The elastic limit of single-phase alloy Nb-2Mo-2Zr-1Ti is higher as recovered state in comparison with as cold-rolled or recrystallized one.For Nb-40Ti-5.5AI alloy of age-hardening type,the elastic limit is lower as cold-rolled state,but increases considerably after proper aging.However,its elastic modulus changes no more,so the stored-energy (σ_e^2/E)may raise significantly.The temperature dependence on elastic modulus for pure Nb as intensely cold-worked or recrystallized state is anomalous.This anomaly may disap- pear after recovered treatment of intensely cold-worked state at 600℃ for 4 h.and may change no more after that of recrystallized state.The anomalous behaviour of elasticity was also discussed on the non-magnetic Nb.
The elastic limit of single-phase alloy Nb-2Mo-2Zr-1Ti is higher as recovered state in comparison with as cold-rolled or recrystallized one.For Nb-40Ti-5.5AI alloy of age-hardening type,the elastic limit is lower as cold-rolled state,but increases considerably after proper aging.However,its elastic modulus changes no more,so the stored-energy (σ_e^2/E)may raise significantly.The temperature dependence on elastic modulus for pure Nb as intensely cold-worked or recrystallized state is anomalous.This anomaly may disap- pear after recovered treatment of intensely cold-worked state at 600℃ for 4 h.and may change no more after that of recrystallized state.The anomalous behaviour of elasticity was also discussed on the non-magnetic Nb.