摘要
The floating phenomenon of MC carbide(TiC)in a hot corrosion resistant single crystal Ni-base superalloy was observed during planar and cellular interface directional solidification.The explanation about the phenomenon is presented.
The floating phenomenon of MC carbide(TiC)in a hot corrosion resistant single crystal Ni-base superalloy was observed during planar and cellular interface directional solidification.The explanation about the phenomenon is presented.