摘要
Diamond-like carbon (DLC) films (a-C:H) were implanted by 140 keV and 110 keV Ar ion beams. The resistivities of the implanted films decreased dramatically under a dose of 2×1016 Ar/cm2 . IR spectra and optical gap Eopt were measured. It was found that the sp2 and sp3 components decreased due to the loss of hydrogen during implantation, and the ratio of components sp bonds to sp bonds increased with the ion dose. And the optical gap Eopt decreased from 1.46 eV to 0.83 eV. The hydrogen (bonded and unbonded) contents in the films were measured with the nuclear resonant reaction 1H(19 F, x 7) 16O. It is shown that hydrogen plays an important role in affecting some properties of DLC fims.
Diamond-like carbon (DLC) films (a-C:H) were implanted by 140 keV and 110 keV Ar ion beams. The resistivities of the implanted films decreased dramatically under a dose of 2×1016 Ar/cm2 . IR spectra and optical gap Eopt were measured. It was found that the sp2 and sp3 components decreased due to the loss of hydrogen during implantation, and the ratio of components sp bonds to sp bonds increased with the ion dose. And the optical gap Eopt decreased from 1.46 eV to 0.83 eV. The hydrogen (bonded and unbonded) contents in the films were measured with the nuclear resonant reaction 1H(19 F, x 7) 16O. It is shown that hydrogen plays an important role in affecting some properties of DLC fims.