摘要
The specific inner surface, S<sub>p</sub>, of the crystalline-amorphous 2-phase system inCu<sub>73</sub>Sn<sub>6</sub>Ni<sub>6</sub>P<sub>15</sub> metallic glass, aged at 473 K, was determined by small-angle X-ray scatteringand wide-angle X-ray diffraction. The experimental results show that the specific innersurface decreases from 144 m<sup>2</sup>/cm<sup>3</sup> to 96 m<sup>2</sup>/cm<sup>3</sup> as aging period increases from 5 min to 4 h.The error of S<sub>p</sub> values is about 7%.
The specific inner surface, S_p, of the crystalline-amorphous 2-phase system inCu_(73)Sn_6Ni_6P_(15) metallic glass, aged at 473 K, was determined by small-angle X-ray scatteringand wide-angle X-ray diffraction. The experimental results show that the specific innersurface decreases from 144 m^2/cm^3 to 96 m^2/cm^3 as aging period increases from 5 min to 4 h.The error of S_p values is about 7%.