The effect of isobutylene-isoprene rubber (IIR) on the crystallizing behavior of isotactic polypropylene (IPP) as well as the morphology of the blends in relation with its properties have been studied by DSC, WAXD, polarized light microscope, SEM and mechanical properties test. The experimental results show that IIR has slight influence on melting point, crystallinity, crystallization rate of IPP. It seems certain that IIR has not entered into IPP phase in melt state. IIR has retarding action on the growth of IPP crystal and is an effective nucleating agent of IPP spherulites. The impact strength of the blend increases rapidly with IIR content more than 30 parts; the tensile strength of the blend, however, decreases as IIR content increases. The temperature and time of alter heat-treatment also have great influence on the impact strength of the blend. The impact strength of IPP/IIR (100/20) heat-treated at about 130℃ for 2h is 5 times as high as that of the untreated blend.
The effect of isobutylene-isoprene rubber (IIR) on the crystallizing behavior of isotactic polypropylene (IPP) as well as the morphology of the blends in relation with its properties have been studied by DSC, WAXD, polarized light microscope, SEM and mechanical properties test. The experimental results show that IIR has slight influence on melting point, crystallinity, crystallization rate of IPP. It seems certain that IIR has not entered into IPP phase in melt state. IIR has retarding action on the growth of IPP crystal and is an effective nucleating agent of IPP spherulites. The impact strength of the blend increases rapidly with IIR content more than 30 parts; the tensile strength of the blend, however, decreases as IIR content increases. The temperature and time of alter heat-treatment also have great influence on the impact strength of the blend. The impact strength of IPP/IIR (100/20) heat-treated at about 130℃ for 2h is 5 times as high as that of the untreated blend.