摘要
The precipitation behaviour of Fe-Cr-Mo and Fe-Cr-W alloys during aging has been ex- perimentally studied.It was found that in the early stage of aging,a metastable R phase pre- cipitated in both alloys,it was transformed into stable μ-phase,Laves-phase,X-phase or σ-phase in the later stages.The crystallographic structure of metastable R-phase is rhombohedral with lattice parameters of a=0.9075 nm and α=74.45°.The chemical compo- sition of R-phase is Fe-(27.5—34.9)Mo-(0—25.5)Cr and Fe-(28.9—33.0)W-(9.36— 21.0)Cr in at.-% in Fe-Cr-Mo and Fe-Cr-W system,respectively.
The precipitation behaviour of Fe-Cr-Mo and Fe-Cr-W alloys during aging has been ex- perimentally studied.It was found that in the early stage of aging,a metastable R phase pre- cipitated in both alloys,it was transformed into stable μ-phase,Laves-phase,X-phase or σ-phase in the later stages.The crystallographic structure of metastable R-phase is rhombohedral with lattice parameters of a=0.9075 nm and α=74.45°.The chemical compo- sition of R-phase is Fe-(27.5—34.9)Mo-(0—25.5)Cr and Fe-(28.9—33.0)W-(9.36— 21.0)Cr in at.-% in Fe-Cr-Mo and Fe-Cr-W system,respectively.