摘要
In this work, the accelerated weathering test of immersion-wet-dry combined cycles was carried ont. The artificial acid rain of NaHSO3-(NH4)2SO4-H2SO4 solution system was selected as immersion solution. Acidity of artificial acid rain affected corrossion weight loss of carbon steel, and pH 4.1 was found to be a critical point. Anodic reaction resistance of the samples during accelerated weathering test increased with exposed time by electrochemical measurement.
In this work, the accelerated weathering test of immersion-wet-dry combined cycles was carried ont. The artificial acid rain of NaHSO3-(NH4)2SO4-H2SO4 solution system was selected as immersion solution. Acidity of artificial acid rain affected corrossion weight loss of carbon steel, and pH 4.1 was found to be a critical point. Anodic reaction resistance of the samples during accelerated weathering test increased with exposed time by electrochemical measurement.