摘要
利用背散射衍射技术(EBSD)和XRD,研究了两段式脱碳退火工艺对取向硅钢纵截面初次再结晶的微区取向、取向差分布、特殊晶界(CSL)及高温退火试样高斯织构。分析了初次再结晶晶界特征对取向硅钢高温退火后宏观织构的影响。结果表明:初次再结晶的纵截面基体中Σ3和Σ5晶界使得高斯晶粒有着较高的迁移率,在高温退火时借助20o~45°的大角度晶界的界面能吞并周围{111}<112>晶粒迅速长大,形成密度水平较高的高斯织构。
Micro area orientation of primary recrystallization,the misorientation distribution,special boundaries under different two-stage decarburization annealing and the Goss texture under high temperature annealing the longitudinal section of grain-oriented silicon steel were detected by electron back scattering diffraction(EBSD) and X-ray diffraction(XRD).The effect of primary recrystallization grain boundary on macrotexture after high temperature annealing was analyzed.The results show that the Σ3 and Σ5 grain boundary make Gaussian grains have higher migration rate in the longitudinal section matrix of the primary recrystallization.And the Gaussian grain swallow up the {111}<112> grains around with the help of the interfacial energy of high-angle boundary of 20°~45°to grow rapidly and form higher density gaussian texture annealing at high temperature.
出处
《材料热处理学报》
EI
CAS
CSCD
北大核心
2013年第S1期97-101,共5页
Transactions of Materials and Heat Treatment
关键词
CSP
取向硅钢
晶界特征
CSP
grain oriented silicon steel
grain boundary characteristics