摘要
Objective:To synthesize silver nanoparticles(AgNPs) by green methods using scrum latex of Calotropis procera at 80 ℃ and evaluate them against bacteria,dermatophytes and phytopathogenic fungi comparing with the activity of untreated latex.Methods:The synthesis of AgNPs was performed by mixing 3%latex scrum extract with the same volume of silver nitrate(2 mmol/L) solution in round flask and heating in water bath at80 ℃.Characterization of silver particles were determined using UV-vis spectrophotometer,transmission electron microscopy(TEM),X-ray diffraction and Fourier transform infrared spectroscopy.The antimicrobial activity of the green synthesized AgNPs was determined against bacteria,dermatophytes and phytopathogenic fungi and compared to the crude untreated latex by agar-well diffusion methods.Results:Biosynthesis of latex silver nanoparticles was successfully obtained by green method.The formation of AgNPs has been confirmed by UV-vis,TEM microscopy.X-ray diffraction and Fourier transform infrared spectroscopy.TEM analysis showed that synthesized AgNPs are highly stable spherical shaped particles,well dispersed with a diameter ranged from 4 nm up to 25 nm and an average size of 12.33 nm.AgNPs showed strong antibacterial activity against Gram-negative bacteria(Escherichia coli,Pseudomonas aeruginosa and Serratia sp.) and antifungal activity against Trichophyton rubrum,Candida albicans and Aspergillus terreus.Conclusions:It can be concluded that serum latex of Calotropis pmcera was found to display strong potential for the synthesis of AgNPs as antimicrobial agents through rapid reduction of silver ions(Ag^+ to Ag^0).The green synthesized AgNPs were found to show higher antimicrobial efficacy than crude latex.
Objective:To synthesize silver nanoparticles(AgNPs) by green methods using scrum latex of Calotropis procera at 80 ℃ and evaluate them against bacteria,dermatophytes and phytopathogenic fungi comparing with the activity of untreated latex.Methods:The synthesis of AgNPs was performed by mixing 3%latex scrum extract with the same volume of silver nitrate(2 mmol/L) solution in round flask and heating in water bath at80 ℃.Characterization of silver particles were determined using UV-vis spectrophotometer,transmission electron microscopy(TEM),X-ray diffraction and Fourier transform infrared spectroscopy.The antimicrobial activity of the green synthesized AgNPs was determined against bacteria,dermatophytes and phytopathogenic fungi and compared to the crude untreated latex by agar-well diffusion methods.Results:Biosynthesis of latex silver nanoparticles was successfully obtained by green method.The formation of AgNPs has been confirmed by UV-vis,TEM microscopy.X-ray diffraction and Fourier transform infrared spectroscopy.TEM analysis showed that synthesized AgNPs are highly stable spherical shaped particles,well dispersed with a diameter ranged from 4 nm up to 25 nm and an average size of 12.33 nm.AgNPs showed strong antibacterial activity against Gram-negative bacteria(Escherichia coli,Pseudomonas aeruginosa and Serratia sp.) and antifungal activity against Trichophyton rubrum,Candida albicans and Aspergillus terreus.Conclusions:It can be concluded that serum latex of Calotropis pmcera was found to display strong potential for the synthesis of AgNPs as antimicrobial agents through rapid reduction of silver ions(Ag^+ to Ag^0).The green synthesized AgNPs were found to show higher antimicrobial efficacy than crude latex.
基金
Supported by Assiut Universityv.Assiut,Egypt