微纳米铁粉热稳定性实验研究 被引量:1

Experimental investigation of micro-nano iron particle on thermal stability
原文传递
导出
摘要 利用管式电阻炉和X射线衍射仪(XRD)实施了对恒温退火处理100、200、300和500 nm 4种粒径的微纳米铁粉热稳定特性实验研究,通过函数拟合衍射峰图谱计算其微观应变,分析退火过程中微纳米铁粉晶粒长大现象。结果表明:微观应变的大小和晶粒长大过程密切相关,随着退火温度升高,微观应变逐渐减小,晶粒尺寸增大。100、200和300 nm微纳米铁粉200℃以下晶粒长大迅速,200℃以上长大速度减小;500 nm铁粉晶粒200℃以下长大速度比较缓慢,200℃以上晶粒迅速长大。低温下大粒径铁粉热稳定性优于小粒径铁粉。 Thermal stability of annealing micro-nano iron particle at an average size of 100 nm,200 nm,300 nm and 500 nm was studied using a tube resistance furnace and an X-ray diffraction( XRD). Microstrain of the iron particles was calculated by selecting a proper function fitting the diffraction peaks and the grain growth was observed on all kinds of samples. Measurement results indicate that microstrain releases with increasing of annealing temperature while crystallite size growing. For the 100 nm,200 nm and 300 nm iron particle,a rapid growth of grain size occurs below 200 ℃,and then the growing speed decreases dramatically with the annealing temperature raising; while for 500 nm iron particle,grain size grows slow below 200 ℃ and then speeds up. These results show that a larger size of iron micro-nano particle has an advantage in thermal stability at low temperature.
出处 《材料热处理学报》 EI CAS CSCD 北大核心 2015年第2期1-4,共4页 Transactions of Materials and Heat Treatment
基金 上海市教委科研重点创新项目(12zzz141) 上海市基础研究重点项目(14JC1404800) 上海理工大学国家级项目培育基金(13XGM09)
关键词 微纳米 热稳定性 晶粒长大 微观应变 micro-nano thermal stability grain growth microstrain
  • 相关文献

参考文献8

二级参考文献59

共引文献200

同被引文献1

引证文献1

二级引证文献3

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部