摘要
用X-射线光电子能谱(XPS)研究铝板/聚丙烯层状复合材料的粘接界面相,提出了粘接界面的化学反应机制.研究发现,聚丙烯(PP)中加入马来酸酐接枝聚丙烯(PP-g-MAH)时,铝板面上Al2p、O1s谱线明显向高结合能端移动,表明PP-g-MAH与铝板表面发生了化学反应,形成Al-O-C配位键.配位键的形成使界面粘接强度明显提高.PP中不含PP-g-MAH时,铝板面上Al2p、O1s谱线处于低结合能端,聚丙烯未与铝板表面形成化学配位作用.
Interphases at the adhesion bonded interfaces between aluminum sheetand polypropylene(PP)/and PP blended with maleic anhydride grafted polypropylene(PP-g-MAH) were studied by X-ray photoelectron spectroscopy(XPS), and a mechanism of coordination bonding at the interfaces was proposed. Compared to PP,for PP with addition of PP-g-MAH the spectra of Al2p and O1s at the surfaceof aluminum sheet shift to higher binding energy obviously,which indicates thatchemical interaction between PP-g-MAH and surface of the aluminum sheet occurs, and as a result Al-O-C bond is formed. There is no chemical interactionbetween PP and surface of the aluminum sheet. The obvious improvement of the adhesion strength between aluminum sheet and PP with PP-g-MAH could be attributed to the formation of Al-O-C bonds.
出处
《物理化学学报》
SCIE
CAS
CSCD
北大核心
2004年第8期882-886,共5页
Acta Physico-Chimica Sinica
基金
湖南省自然科学基金(03JJY3075)资助项目~~
关键词
铝板/聚丙烯复合材料
马来酸酐接枝聚丙烯
界面相
配位键
X射线光电子能谱
Aluminum sheet/polypropylene laminated composite, Maleic anhydride grafted polypropylene(PP-g-MAH), Interphase, Coordinative bond, X-ray photoelectron spectroscopy(XPS)