摘要
In the view of crystallization activation energy of amorphous alloy, the mechanism of coarse grain in annealed Sm 5Fe 80Cu 1Si 5B 3C 2.5Zr 3.5 amorphous alloy was analyzed. It reveals the effect of preannealing on the process crystallization. The results show that preannealing can be used to change the crystallization behavior of the α-Fe phase in the Sm 5Fe 80Cu 1Si 5B 3C 2.5Zr 3.5 amorphous alloy, which is helpful for forming α-Fe phase grains; and it is not large for Sm 2Fe 17C x phase.
In the view of crystallization activation energy of amorphous alloy, the mechanism of coarse grain in annealed Sm 5Fe 80Cu 1Si 5B 3C 2.5Zr 3.5 amorphous alloy was analyzed. It reveals the effect of preannealing on the process crystallization. The results show that preannealing can be used to change the crystallization behavior of the α-Fe phase in the Sm 5Fe 80Cu 1Si 5B 3C 2.5Zr 3.5 amorphous alloy, which is helpful for forming α-Fe phase grains; and it is not large for Sm 2Fe 17C x phase.
出处
《中国有色金属学会会刊:英文版》
CSCD
2002年第5期854-857,共4页
Transactions of Nonferrous Metals Society of China
基金
Project( 199740 35 )supportedbytheNationalNaturalScienceFoundationofChina
project( 5 992 40 )supportedbytheNaturalScienceFoundationofHebeiProvinceandproject(GG -4 30 -10 2 16 -16 78)supportedbytheFoundationofMinistryofEducationforKeyTeachers
关键词
钐铁铜硅硼碳
锆玻璃态合金
预退火
结晶法
Sm 5Fe 80Cu 1Si 5B 3C 2.5Zr 3.5 amorphous alloy
preannealing
crystallization