The laser beam welding of BT20 titanium alloy was conducted to investigate the weld shape, microstructures and properties. The full penetration weld characteristics produced by CO_2 laser and by YAG laser were compared. The results show that the full penetration weld of YAG laser welding closes to “X” shape, and weld of CO_2 laser welding is “nail-head” shape. Those result from special heating mode of laser deep penetration welding. The tension strength of CO_2 laser and YAG laser joints equal to that of the base metal, but the former has better ductility. All welds consist mainly of the acicular α phase and a few β phase in microstructure. The dendritic crystal of CO_2 laser weld is a little finer than YAG laser weld. According the research CO_2 laser is better than YAG laser for welding of BT20 titanium alloy.
The laser beam welding of BT20 titanium alloy was conducted to investigate the weld shape, microstructures and properties. The full penetration weld characteristics produced by CO_2 laser and by YAG laser were compared. The results show that the full penetration weld of YAG laser welding closes to “X” shape, and weld of CO_2 laser welding is “nail-head” shape. Those result from special heating mode of laser deep penetration welding. The tension strength of CO_2 laser and YAG laser joints equal to that of the base metal, but the former has better ductility. All welds consist mainly of the acicular α phase and a few β phase in microstructure. The dendritic crystal of CO_2 laser weld is a little finer than YAG laser weld. According the research CO_2 laser is better than YAG laser for welding of BT20 titanium alloy.