Cu47Ti34Zr11Ni8块体非晶合金的热稳定性和力学性能 被引量:8

Thermal stability and mechanical properties of Cu47Ti34Zr11Ni8 bulk amorphous alloys
下载PDF
导出
摘要 采用差压铸造法成功制备了Cu47Ti34Zr11Ni8块体非晶合金,研究了其热稳定性和力学性能。结果表明:=735K,过冷液相区ΔTx=63K,约化玻璃温度Trg=0.该块体非晶合金的玻璃转变温度Tg=672K,晶化温度Tx1575,弯曲断裂强度高达2350MPa,断裂前弹性变形量为2.1%,弯曲模量为102GPa;淬态微米级结晶相的出现使合金的三点弯曲断裂强度下降至1100MPa。 Cu47Ti34Zr11Ni8 bulk amorphous alloy was prepared by differential pressure casting. Thermal stability and mechanical properties were studied. The results show that the glass transition temperature(T_g), crystallization temperature(T_x_1), temperature interval of supercooled liquid region ΔT_x(=T_x_1-T_g) and reduced glass transition temperature(T_rg) are proved to be 672 K, 735 K, 63 K, and 0.575, respectively. The bulk glass also exhibits high three point-bending flexural strength of 2 350 MPa, flexural modulus of 102 GPa and fracture strain of 2.1%. The three point-bending flexural strength of the alloys declines to 1 100 MPa with the appearance of a micron-size quenched-in crystallization.
出处 《中国有色金属学报》 EI CAS CSCD 北大核心 2004年第9期1585-1589,共5页 The Chinese Journal of Nonferrous Metals
基金 江苏省自然科学基金资助项目(BK2001053) 南京理工大学科研发展基金资助项目(AB96054)
关键词 块体非晶合金 玻璃形成能力 力学性能 bulk amorphous alloy glass-forming ability(GFA) mechanical properties
  • 相关文献

参考文献15

  • 1Klement W, Willens R H, Duwez P. Non-crystalline structure in solidified gold-silicon alloys [J]. Nature,1960, 187: 869-870.
  • 2Inoue A, Kohinata M, Tsai A P, et al. Mg-Ni-La amorphous alloys with a wide supercooled liquid region [J]. Mater Trans JIM, 1989, 30: 378-381.
  • 3Peker A, Johnson W L. A highly processable metallic glass: Zr41.2Ti13.8Cu12.5Ni10.0Be22.5[J]. Appl Phys Lett, 1993, 63: 2342-2344.
  • 4Inoue A, Nishiyama N, Amiya K, et al. Ti-based amorphous alloys with a wide supercooled liquid region [J]. Mater Lett, 1994, 19: 131-135.
  • 5Inoue A, Gook J S. Fe-based ferromagnetic glassy alloys with wide supercooled liquid region[J]. Mater Trans JIM, 1995, 36: 1180- 1183.
  • 6Inoue A, Katuya A. Multicomponent Co-based amorphous alloys with wide supercooled liquid region[J].Mater Trans JIM, 1996, 37:1332 - 1336.
  • 7Wang X M, Yoshii I, Inoue A. Bulk amorphous CoNi-based alloys with a large supercooled liquid region [J]. Mater Trans JIM, 2000, 41:539 -542.
  • 8Lin X H, Johnson W L. Formation of Ti-Zr-Cu-Ni bulk metallic glasses[J]. J Appl Phys, 1995, 78(11):6514 - 6519.
  • 9Bae D H, Lim H K, KimS H, et al. Mechanical behavior of a bulk Cu-Ti-Zr-Ni-Si-Sn metallic glass forming nano-crystal aggregate bands during deforming in the supercooled liquid region[J]. Acta Mater, 2002,50: 1749- 1759.
  • 10Calin M, Eckert J, Schultz L. Improved mechanical behavior of Cu-Ti-based bulk metallic glass by in situ forming of nanoscale precipitates[J]. Scripta Mater,2003, 48:653 - 658.

同被引文献89

引证文献8

二级引证文献44

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部