摘要
简要分析了催化裂化再生系统设备腐蚀开裂的原因,探讨了现在实施的几种防护措施及出现的问题,并且提出改进防护措施。
The reasons for the corrosion cracking that occurred in the equipment of catalytic cracking regenerating system are analyzed. Several prevailing protective measures at present and their relevant problems are discussed. An improved protective measure is presented.
出处
《腐蚀与防护》
CAS
2004年第10期429-431,共3页
Corrosion & Protection
关键词
催化裂化再生器
开裂
原因
防护措施
Catalytic cracking regenerator
Cracking
Reason
Protective measure