摘要
以聚砜微孔膜为增强体制备增强的氧化锆纤维隔膜材料,可使布膜的强度由原来的102g/cm(宽)提高到现在的198g/cm(宽),吸碱速率由原来的2cm/min提高到现在的4cm/min,而其它的性能如厚度、孔隙率及面电阻等基本不受影响,研制的氧化锆纤维碱性电池隔膜材料基本满足工程化应用的要求。
Strengthened with polysulfone (PS) ultra filtration membrane, the tensile strength of the zirconia fiberseparator material was improved from 102g/cm(width) to 198g/cm(width), the alkali absorption was improved from2cm/min to 4cm/min and the other performances, such as the thickness, porosity and surface resistance, were not af-fected. The zirconia fiber film prepared almost can meet the requirements for the application of spacecraft engineering.
出处
《硅酸盐通报》
CAS
CSCD
2004年第5期20-23,共4页
Bulletin of the Chinese Ceramic Society