摘要
Sr-5LaTi-3Nb-7O- 30 ceramic was prepared by the conventional high temperature solid-state reaction route. The sintered samples were characterized by X-ray diffraction, scanning electron microscopy (SEM), differential thermal calorimetry (DSC) and dielectric measurements.The results show Sr-5LaTi-3Nb-7O- 30 belongs to paraelectric phase of filled tetragonal TB structure at room temperature, and undergoes a diffuse phase transition in the temperature range of -54-34 ℃.And Sr-5LaTi-3Nb-7O- 30 ceramic shows a high dielectric constant of 479 with a low dielectric loss of 0.005 at 1MHz. In comparison with Ba-based ceramics with TB structure, the temperature coefficients of the dielectric constant (τ-ε) is significantly reduced.
Sr-5LaTi-3Nb-7O- 30 ceramic was prepared by the conventional high temperature solid-state reaction route. The sintered samples were characterized by X-ray diffraction, scanning electron microscopy (SEM), differential thermal calorimetry (DSC) and dielectric measurements.The results show Sr-5LaTi-3Nb-7O- 30 belongs to paraelectric phase of filled tetragonal TB structure at room temperature, and undergoes a diffuse phase transition in the temperature range of -54-34 ℃.And Sr-5LaTi-3Nb-7O- 30 ceramic shows a high dielectric constant of 479 with a low dielectric loss of 0.005 at 1MHz. In comparison with Ba-based ceramics with TB structure, the temperature coefficients of the dielectric constant (τ-ε) is significantly reduced.
基金
FundedbytheNationalNaturalScienceFoundationofChi na (N0 .5 0 0 0 2 0 0 7)