摘要
Ba2ZnxCo2-xFe12O22 hexaferrites with x = 0.0, 0.4, 0.8, 1.2, 1.6 and 2.0 were prepared by citrate sol-gel process. The complex dielectric constant and complex permeability of hexaferrites were studied as functions of the measuring frequency, composition and sintering temperature in the range 100 MHz similar to 6 GHz. The natural resonance phenomenon is observed in mu' spectrum for all Y-type hexaferrites, which resonance frequency is dependent on zinc content and firing temperature. The natural resonance frequencies Of Co2Y hexaferrite were calculated, which is in agreement with the measuring results. The reflection loss of those ferrites is measuring frequency as well as absorber thickness dependent, and the higher the frequency and the thickness are, the higher the reflection loss is.
Ba2ZnxCo2-xFe12O22 hexaferrites with x = 0.0, 0.4, 0.8, 1.2, 1.6 and 2.0 were prepared by citrate sol-gel process. The complex dielectric constant and complex permeability of hexaferrites were studied as functions of the measuring frequency, composition and sintering temperature in the range 100 MHz similar to 6 GHz. The natural resonance phenomenon is observed in mu' spectrum for all Y-type hexaferrites, which resonance frequency is dependent on zinc content and firing temperature. The natural resonance frequencies Of Co2Y hexaferrite were calculated, which is in agreement with the measuring results. The reflection loss of those ferrites is measuring frequency as well as absorber thickness dependent, and the higher the frequency and the thickness are, the higher the reflection loss is.
基金
ProjectsupportedbyNationalNaturalScienceFoundationofChina ( 5 9995 3 2 0 .4)