摘要
It has been found that magnetic property changes in austenitic stainless steel subjected to creep at high temperature. The change of magnetic property is mainly due to decrease the chromium concentration in the vicinity of grain boundary and transform into martensite in the area. However this result is for short-term creep. It is necessary to evaluate the long-term creep in order to develop non-destructive technique for plants. Moreover it is important to evaluate the fatigue. The change of magnetic property for those damages at high temperatures is investigated. The transformation into martensite is observed for both the long-term creep and fatigue. The magnetic regions are observed in sever deformed area and near crack. Then the formation of magnetic phases is related to the damage. The damage at high temperature can be universally evaluated.
It has been found that magnetic property changes in austenitic stainless steel subjected to creep at high temperature. The change of magnetic property is mainly due to decrease the chromium concentration in the vicinity of grain boundary and transform into martensite in the area. However this result is for short-term creep. It is necessary to evaluate the long-term creep in order to develop non-destructive technique for plants. Moreover it is important to evaluate the fatigue. The change of magnetic property for those damages at high temperatures is investigated. The transformation into martensite is observed for both the long-term creep and fatigue. The magnetic regions are observed in sever deformed area and near crack. Then the formation of magnetic phases is related to the damage. The damage at high temperature can be universally evaluated.