摘要
The present study aims at developing high speed steel (HSS) as roll materialsto replace traditional roll materials such as the alloy cast iron and powder metallurgical (PM)hard alloy, because low-cost alloy cast iron rolls have poor wear resistance and the cost ofhigh-quality PM hard alloy rolls is too high to be accepted by some users. By means of a centrifugalcasting method, HSS rolls with excellent wear resistance have been developed. Its hardness is 65-67 HRC, and its variation is smaller than 2HRC; its impact toughness excels 15J/cm^2. Usingpre-finishing stands of a high-speed hot wire-rod rolling mill, the wear rate of HSS rolls per onethousand ton of steel is 0. 25mm. However, the manufacturing burden of HSS rolls is obviously lowerthan that of PM hard alloy rolls; it is only 30% of that of PM hard alloy rolls.
The present study aims at developing high speed steel (HSS) as roll materialsto replace traditional roll materials such as the alloy cast iron and powder metallurgical (PM)hard alloy, because low-cost alloy cast iron rolls have poor wear resistance and the cost ofhigh-quality PM hard alloy rolls is too high to be accepted by some users. By means of a centrifugalcasting method, HSS rolls with excellent wear resistance have been developed. Its hardness is 65-67 HRC, and its variation is smaller than 2HRC; its impact toughness excels 15J/cm^2. Usingpre-finishing stands of a high-speed hot wire-rod rolling mill, the wear rate of HSS rolls per onethousand ton of steel is 0. 25mm. However, the manufacturing burden of HSS rolls is obviously lowerthan that of PM hard alloy rolls; it is only 30% of that of PM hard alloy rolls.
基金
ThisworkwassupportedbytheUniversityYoungBackboneTeacherProgramofHenanProvince
theTackle Key ProgramofS&TCommitteeofHenanProvinceunderGrantNo .0 4 2 4 2 6 0 0 0 2
theNationalHigh TechR&DProgramforCIMSofChinaunderGrantNo .2 0 0 2AA4 15 2 5 0
and