A novel fullerene-acrylamide copolymer was synthesized via radical polymerization. It is soluble in polar sol- vents such as water, dimethyl sulfoxide etc. The product was characterized by FTIR, UV-Vis and GPC. TEM analy- sis shows that the average particle diameter is about 46 nm. Four-ball tests show that the addition of a certain con- centration of the fullerene copolymer to base stock (2 wt% triethanolamine and 0.5 wt% OPZ aqueous solution) can effectively raise the load-carrying capacity (PB value) and the antiwear ability. SEM analysis shows that the addition results in reducing diameter of wear scar and decreasing wear.
A novel fullerene-acrylamide copolymer was synthesized via radical polymerization. It is soluble in polar sol- vents such as water, dimethyl sulfoxide etc. The product was characterized by FTIR, UV-Vis and GPC. TEM analy- sis shows that the average particle diameter is about 46 nm. Four-ball tests show that the addition of a certain con- centration of the fullerene copolymer to base stock (2 wt% triethanolamine and 0.5 wt% OPZ aqueous solution) can effectively raise the load-carrying capacity (PB value) and the antiwear ability. SEM analysis shows that the addition results in reducing diameter of wear scar and decreasing wear.
基金
Project supported by the National Natural Science Foundation of China (No. 20074012) and Anhui Provincial Universities Natural Science Founda-tion (No. 2002kj290).