摘要
s Ba_4Zn_zCo_(2-z)Fe_(36)O_(60) hexaferrites with Z = 2.0, 1.5, 1.0, 0.5, and0.0 were prepared by a citrate Sol-gel process. The complex dielectric constant and complexpermeability of hexaferrite-paraffin wax composites were measured in the range from 0.1 to 6.0 GHz.Measured results showed that both the complex dielectric constant and the dielectric loss exhibitedno significant change as the measuring frequency increasing except for the sample with Z = 0.0. Thereal part of permeability decreased with increasing frequency for all samples in the whole measuringfrequency range, and the natural resonance phenomena were observed in all μ″ spectrum but Co_2U.The results also indicate that the content of zinc closely affects the microwave properties ofBa_4Zn_zCo_(2-z)Fe_(36)O_(60) ferrites, and the greater the zinc content, the lower the naturalresonance frequency is.
s Ba_4Zn_zCo_(2-z)Fe_(36)O_(60) hexaferrites with Z = 2.0, 1.5, 1.0, 0.5, and0.0 were prepared by a citrate Sol-gel process. The complex dielectric constant and complexpermeability of hexaferrite-paraffin wax composites were measured in the range from 0.1 to 6.0 GHz.Measured results showed that both the complex dielectric constant and the dielectric loss exhibitedno significant change as the measuring frequency increasing except for the sample with Z = 0.0. Thereal part of permeability decreased with increasing frequency for all samples in the whole measuringfrequency range, and the natural resonance phenomena were observed in all μ″ spectrum but Co_2U.The results also indicate that the content of zinc closely affects the microwave properties ofBa_4Zn_zCo_(2-z)Fe_(36)O_(60) ferrites, and the greater the zinc content, the lower the naturalresonance frequency is.
基金
This work was financially supported by the National Natural Science Foundation of China (No. 59995320.4).