Acicular ferrite microstructure was achieved for an ultralow carbon pipeline steel through the improved thermome chanical control process (TMCP), which was based on the transformation process of deformed austenite of steel. Compared with commercial pipeline steels, the experimental ultralow carbon pipeline steel possessed the satisfied strength and toughness behaviors under the current improved TMCP, although it contained only approximately 0.025% C, vvhich should mainly be attributed to the microstructural characteristics of acicular ferrite.
Acicular ferrite microstructure was achieved for an ultralow carbon pipeline steel through the improved thermome chanical control process (TMCP), which was based on the transformation process of deformed austenite of steel. Compared with commercial pipeline steels, the experimental ultralow carbon pipeline steel possessed the satisfied strength and toughness behaviors under the current improved TMCP, although it contained only approximately 0.025% C, vvhich should mainly be attributed to the microstructural characteristics of acicular ferrite.
基金
The present work was financially supported by a China National‘973’Project No.G1998061511
the Natural Science Fund of Hebei Province No.501205.