摘要
A nitrate-citrate combustion route to synthesize La0.9Sr0.1Ga0.8Mg0.2O3-σ powder for solid oxide fuel cell application was presented. This route is based on the gelling of nitrate solutions by the addition of citric acid and ammonium hydroxide, followed by an intense combustion process due to an exothermic redox reaction between nitrate and citrate ions. The optimum technical parameters are that the pH value is 5, and the molar ratio of citric acid to the total metallic ion is 1.5:1. X-ray diffraction characterization of calcined gel shows that pure phase was synthesized after calcination at 1400℃for 10 h, and the TEM result shovvs the calcined powder with average particle size is about 150 nm. The grain resistance contributes to the total resistance of sintered peliet below 500℃. The conductivity of the sintered peliet at 800℃ was 0.07 S-1·cm-1 higher than the conductivity of YSZ (0.05 S-1·cm-1 at 800℃)
A nitrate-citrate combustion route to synthesize La0.9Sr0.1Ga0.8Mg0.2O3-σ powder for solid oxide fuel cell application was presented. This route is based on the gelling of nitrate solutions by the addition of citric acid and ammonium hydroxide, followed by an intense combustion process due to an exothermic redox reaction between nitrate and citrate ions. The optimum technical parameters are that the pH value is 5, and the molar ratio of citric acid to the total metallic ion is 1.5:1. X-ray diffraction characterization of calcined gel shows that pure phase was synthesized after calcination at 1400℃for 10 h, and the TEM result shovvs the calcined powder with average particle size is about 150 nm. The grain resistance contributes to the total resistance of sintered peliet below 500℃. The conductivity of the sintered peliet at 800℃ was 0.07 S-1·cm-1 higher than the conductivity of YSZ (0.05 S-1·cm-1 at 800℃)
基金
The authors acknowledge financial support from 863 National Project(No.2003AA302440).