研究了高强碳纤维镀Ni和镀NiCuMn对C/Al扩散焊界面结合性能的影响,重点分析了Mn元素提高C/Al界面结合性能的机理,并根据不同锰含量下的δ和σc值,建立了δ与σc的数学模型。
The interface of diffusion bonding C/Al composite reinforced with Ni plated and NiCuMn multiplated high strength carbon fibers are investigted, the mechanism of Mn element enhancing the bond of C/Al interface is analyzed and a relationship of the thicknssδ of interfacial active layer with fracture stress of the sample is estabished.