LPCNi 3.55 Co 0.75 Mn 0.4 Al 0.3 hydrogen storage alloy was investigated, and the effects of thickness of its strip casting ingots(as cast) on the electrochemical performances were discussed. It was found that the 0.2 C discharge capacity increased with the increase of the thickness (from 1 mm to 10 mm) of the ingots, mainly due to the enlargement of the unit cell volume; Among the thickness of the ingots in our study, 10 mm sample showed a better activation property; LPCNi 3.55 Co 0.75 Mn 0.4 Al 0.3 alloy with 10mm showed higher comprehensive properties than those with other thickness under 1C rate.
LPCNi 3.55 Co 0.75 Mn 0.4 Al 0.3 hydrogen storage alloy was investigated, and the effects of thickness of its strip casting ingots(as cast) on the electrochemical performances were discussed. It was found that the 0.2 C discharge capacity increased with the increase of the thickness (from 1 mm to 10 mm) of the ingots, mainly due to the enlargement of the unit cell volume; Among the thickness of the ingots in our study, 10 mm sample showed a better activation property; LPCNi 3.55 Co 0.75 Mn 0.4 Al 0.3 alloy with 10mm showed higher comprehensive properties than those with other thickness under 1C rate.
基金
ProjectsupportedKeySci .&Tech .R&DofSichuanPlannedCommittee ( 1 1 91 ( 1 997) )