Surface modification of microporous polypropylene hollow fiber membranes was performed by radical-induced graft polymerization of N,N-dimethylaminoethyl methacrylate (DMAEMA). The influences of temperature, monomer concentration and pre-adsorbed amount of benzoyl peroxide on grafting degree were studied respectively. It was found that the appropriate graft temperature was 75 'C, at which the grafting degree was the highest and the hydrolytic decomposition of DMAEMA the lowest. Scanning electron photomicrography and the average pore diameters of the modified membranes demonstrated that part of the micropores on the membrane surface was plugged by the grafted polyDMAEMA chains, especially at high grafting degree. Contact angle and water swelling experiments showed that a moderate grafting degree could improve the hydrophilicity of the membranes. In the range of 11.3%-12.0% grafting degree, the water swelling percentage reached its maximum (51.1%) and the contact angle reached its minimum (74 degrees). The bovine serum albumin (BSA) adsorption experiment indicated that the grafted polyDMAEMA had a dual effect on protein adsorption. At the first stage, the BSA adsorption decreased with increasing of DMAEMA grafting degree. As the interaction between BSA and polyDMAEMA on membrane surface increased, the BSA adsorption increased with increasing of DMAEMA grafting degree.
Surface modification of microporous polypropylene hollow fiber membranes was performed by radical-induced graft polymerization of N,N-dimethylaminoethyl methacrylate (DMAEMA). The influences of temperature, monomer concentration and pre-adsorbed amount of benzoyl peroxide on grafting degree were studied respectively. It was found that the appropriate graft temperature was 75 'C, at which the grafting degree was the highest and the hydrolytic decomposition of DMAEMA the lowest. Scanning electron photomicrography and the average pore diameters of the modified membranes demonstrated that part of the micropores on the membrane surface was plugged by the grafted polyDMAEMA chains, especially at high grafting degree. Contact angle and water swelling experiments showed that a moderate grafting degree could improve the hydrophilicity of the membranes. In the range of 11.3%-12.0% grafting degree, the water swelling percentage reached its maximum (51.1%) and the contact angle reached its minimum (74 degrees). The bovine serum albumin (BSA) adsorption experiment indicated that the grafted polyDMAEMA had a dual effect on protein adsorption. At the first stage, the BSA adsorption decreased with increasing of DMAEMA grafting degree. As the interaction between BSA and polyDMAEMA on membrane surface increased, the BSA adsorption increased with increasing of DMAEMA grafting degree.
基金
The work was supported by the National Natural Science Foundation of China (Grant No. 20074033) and the High-TechResearch and Development Program of China (Grant no. 2002AA601230).