摘要
目的 通过开环共聚方法合成三嵌段共聚物 (PEG- PL GA- PEG,简称 PEL GE)。采用超声乳化—溶剂蒸发法 (O/ W)制备 PEL GE纳米粒。方法 对可能影响纳米粒粒径大小的因素 ,如有机相和水相的体积比、聚合物的浓度、表面活性剂的浓度等做了较详细的考察。结果 其优选方案为 :高分子载体材料的质量浓度为 10 m g/ml,有机溶剂为丙酮 /二氯甲烷 (体积比为 2 / 3)的混合溶剂 ,F6 8溶液的质量浓度为 30 g/ L,油相与水相体积比为1∶ 8。结论 制备的纳米粒大小均匀 ,呈规整球形 ,粒径分布范围为 6 0~ 10 0 nm。
Objective To prepare Poly(ethylene glycol) - poly (lacticacid-co-glycolicacid)- poly(ethylene- glycol) nanoparticles (PELGE-NP) and investigate the factors affecting their diameter. Methods PELGE were synthesized by ring-opening polymerization, PELGE nanoparticles(PELGE-NP) were prepared by using the emulsion-solvent evaporation technique (O/W). Orthogonal design was applied to optimize the preparation technology on the basis of the single factor evaluation. Results The optimal conditions for preparing nanoparticles included the PELGE at concentration of 10 mg/ml, the ratio of acetone/DCM at 2/3, the F68 at concentration of 3%, and the volume ratio of O/W at 1/8(V/V). Conclusion The prepared PELGE nanoparticles are spherical and discrete particles without aggregation; they are smooth in surface morphology, and their diameters range from 60 nm to 100 nm.
出处
《四川大学学报(医学版)》
CAS
CSCD
北大核心
2005年第1期115-118,共4页
Journal of Sichuan University(Medical Sciences)
基金
国家"十五"重大科技专项课题 (批准号 2 0 0 4AA2 73 14 2 )资助
关键词
纳米粒
PELGE
乳化-溶剂蒸发
Nanoparticles PELGE Emulsion-solvent evaporation technique