摘要
测试了研制的绿色缓蚀剂在中性3.5%NaCl水溶液中抑制3种钢的应力腐蚀开裂(SCC)和腐蚀疲劳(CF)断裂的能力,结果表明抑制SCC的能力超过铬酸盐、磷酸盐的水平,抑制CF的能力则与研制缓蚀剂的配方有关。
In this work the abilities of developed inhibitors against both stress corrosion cracking(SCC) and corrosion fatigue(CF) for three types of steel were examined. In neutral 3.5%NaCl solution, the inhibiting abilities against SCC were better than those of chromates and phosphate. However, the ability against CF were dependent on the inhibitor formulation.
出处
《腐蚀与防护》
CAS
北大核心
2005年第1期10-12,共3页
Corrosion & Protection
关键词
绿色缓蚀剂
防锈颜料
铬酸盐
应力腐蚀
腐蚀疲劳
Green inhibitor
Inhibiting pigment
Chromate
Stress corrosion cracking
Corrosion fatigue