A series of Ce-doped Ni-B amorphous alloy catalysts were prepared by a KBH_4 reduction method, characterized by ICP, BET, XRD, H_2-chemisorption, H_2-TPD, etc., and tested in the hydrogenation of 2-ethylanthraquinone. The results of characterization show that with the addition of Ce the amount of H_2-chemisorption and H_2-TPD areas first increases markedly and then decreases with the maximum appears at the atomic ratio of Ce to Ni of 0.036. The hydrogenation activity also shows the same trend. The effects of Ce are attributed to its dispersion of Ni particles, resulting in the formation of more surface Ni centers. However, much higher Ce contents may result in the decrease of the surface Ni contents. After heat treatment at higher temperatures, the amorphous structure of Ni-B is destroyed.
A series of Ce-doped Ni-B amorphous alloy catalysts were prepared by a KBH_4 reduction method, characterized by ICP, BET, XRD, H_2-chemisorption, H_2-TPD, etc., and tested in the hydrogenation of 2-ethylanthraquinone. The results of characterization show that with the addition of Ce the amount of H_2-chemisorption and H_2-TPD areas first increases markedly and then decreases with the maximum appears at the atomic ratio of Ce to Ni of 0.036. The hydrogenation activity also shows the same trend. The effects of Ce are attributed to its dispersion of Ni particles, resulting in the formation of more surface Ni centers. However, much higher Ce contents may result in the decrease of the surface Ni contents. After heat treatment at higher temperatures, the amorphous structure of Ni-B is destroyed.
基金
ProjectsupportedbytheStateKeyFundamentalResearchProjectofChina (G2 0 0 0 0 480 0 5 )andtheNationalNaturalScienceFoundationofChina ( 2 9873 0 40 )