The fatigue contrast tests of unload longitudinal direction comer joints asoriginal welded and treated by ultrasonic peening of Q235B in various stress ratio are directed. Theimprovements of fatigue performance of unload longitudinal direction corner joints resulted byultrasonic peening are studied. The effect pattern of stress ratio on fatigue performance of weldedjoints that are treated by ultrasonic peening is studied. As tests results indicate that: ① In thecondition of stress ratio .R=-l, the fatigue strength 'of specimen treated by ultrasonic peening isincreased by 165 percent of that of the original welded specimen. And the fatigue life of specimentreated by ultrasonic peening is as much as 75 approx 210 times of that of the latter. When R=0.1,the fatigue strength is increased by 87 percent and the fatigue life is extended by 21 approx 29times. When R=-0.5, the fatigue strength is increased by 123 percent and the fatigue life isextended by 42 approx 59 times. When R=0.45, the fatigue strength is increased by 51 percent and thefatigue life is extended by 3 approx 14 times. ② If the welded joints are treated by ultrasonicpeening, the fatigue strength is no longer independent on the applied mean stress. The more thestress ratio R, the less the fatigue stress range which can be sustained by the joints is. ③Whether the high value residual stress is in the joints or not, the dead load portion of the appliedload must be considered in the design of the joints which should be treated by ultrasonic peening.
The fatigue contrast tests of unload longitudinal direction comer joints asoriginal welded and treated by ultrasonic peening of Q235B in various stress ratio are directed. Theimprovements of fatigue performance of unload longitudinal direction corner joints resulted byultrasonic peening are studied. The effect pattern of stress ratio on fatigue performance of weldedjoints that are treated by ultrasonic peening is studied. As tests results indicate that: ① In thecondition of stress ratio .R=-l, the fatigue strength 'of specimen treated by ultrasonic peening isincreased by 165 percent of that of the original welded specimen. And the fatigue life of specimentreated by ultrasonic peening is as much as 75 approx 210 times of that of the latter. When R=0.1,the fatigue strength is increased by 87 percent and the fatigue life is extended by 21 approx 29times. When R=-0.5, the fatigue strength is increased by 123 percent and the fatigue life isextended by 42 approx 59 times. When R=0.45, the fatigue strength is increased by 51 percent and thefatigue life is extended by 3 approx 14 times. ② If the welded joints are treated by ultrasonicpeening, the fatigue strength is no longer independent on the applied mean stress. The more thestress ratio R, the less the fatigue stress range which can be sustained by the joints is. ③Whether the high value residual stress is in the joints or not, the dead load portion of the appliedload must be considered in the design of the joints which should be treated by ultrasonic peening.
基金
ThisprojectissupportedbyNationalNaturalScienceFoundationofChina(No.59575061)