摘要
从生产的机理和如何控制等方面对沾锡、光畸变、虹彩三种缺陷进行了分析和探讨,着重阐述了对锡槽 锡液中含氧量的控制方法和措施,在提高浮法玻璃质量,防止浮法玻璃污染,减少玻璃表面缺陷等方面采取切实 可靠的技术措施。
Three kinds of defects , i. e. tin pickup , light distortion and bloom , were discussed from aspects of both production mechanism and control methods . The controlling means of oxygen content in tin bath was stressed . Some technical measures to improve glass quality , prevent contamination and diminish surface defect were also emphasized .