摘要
Electrochemical polymerizations of various ratios of pyrrole and methylpyrrole monomers were performed in aqueous toluene-4-sulfinic acid sodium salt (T4SNa) electrolyte, using galvanostatic method. pH of electrolyte was adjusted by p-toluene sulfonic acid (PTSA). In order to prevent corrosion of mild steel substrates during coating deposition, specimens were pretreated in 0.5M oxalic acid solution, employing galvanostatic method. This would passivate the steel substrate and facilitate the coating process as well. Corrosion resistance of coated substrates was investigated in 1M NaCl solution using Tafel polarization technique. In addition, using scanning electron microscopy (SEM), morphological characterization of coatings produced, was investigated. Regarding the corrosion characteristics, results obtained revealed that the ratio of 1 to 1 (Pyrrole/Methylpyrrole) could play an important role.
Electrochemical polymerizations of various ratios of pyrrole and methylpyrrole monomers were performed in aqueous toluene-4-sulfinic acid sodium salt (T4SNa) electrolyte, using galvanostatic method. pH of electrolyte was adjusted by p-toluene sulfonic acid (PTSA). In order to prevent corrosion of mild steel substrates during coating deposition, specimens were pretreated in 0.5M oxalic acid solution, employing galvanostatic method. This would passivate the steel substrate and facilitate the coating process as well. Corrosion resistance of coated substrates was investigated in 1M NaCl solution using Tafel polarization technique. In addition, using scanning electron microscopy (SEM), morphological characterization of coatings produced, was investigated. Regarding the corrosion characteristics, results obtained revealed that the ratio of 1 to 1 (Pyrrole/Methylpyrrole) could play an important role.
出处
《材料热处理学报》
EI
CAS
CSCD
北大核心
2004年第05B期1137-1141,共5页
Transactions of Materials and Heat Treatment
关键词
导电聚合物
电引发聚合
吡咯
耐蚀性
低碳钢
Conductive polymer, electropolymerization, pyrrole, N-methylpyrrole, corrosion