The fretting wear behavior of plasma spraying CoCrW and Cr3C2-NiCr coatings were investigated. The results showed both plasma spraying coatings were inferior to K417 nickel superalloy in the fretting wear resistance. The characterized fatigue delamination of the plasma sprayed coatings was evidently different from that of the homogeneous materials. The lamellar cohesion, oxide inclusions and porosity were critical factors that controlled the fretting wear resistance. In the view of contact mechanics, the fretting wear behavior of plasma spraying coatings was characterized.
The fretting wear behavior of plasma spraying CoCrW and Cr3C2-NiCr coatings were investigated. The results showed both plasma spraying coatings were inferior to K417 nickel superalloy in the fretting wear resistance. The characterized fatigue delamination of the plasma sprayed coatings was evidently different from that of the homogeneous materials. The lamellar cohesion, oxide inclusions and porosity were critical factors that controlled the fretting wear resistance. In the view of contact mechanics, the fretting wear behavior of plasma spraying coatings was characterized.
出处
《材料热处理学报》
EI
CAS
CSCD
北大核心
2004年第05B期960-963,共4页
Transactions of Materials and Heat Treatment
关键词
等离子喷涂
摩擦磨损
疲劳特性
接触力学
Plasma spraying, Coating, Fretting wear, Fatigue delamination, Contact mechanics