The effect of the content of rare-earth La on the microstructure and corrosion-resistance of hot-dipped aluminum was investigated in this paper. The results show that, under the same technology conditions, the thickness of hot-dipped aluminizing layer by adding the appropriate content of rare-earth La is about 2～3 times as much as that without rare-earth La, and the microstructure of hot-dipped aluminizing layer has also greatly changed ,and a great deal of phase Fe3Al was precipitated along the boundary of α phase. The corrosion resistance of the hot-dipped layer with rare-earth is greatly increased.
The effect of the content of rare-earth La on the microstructure and corrosion-resistance of hot-dipped aluminum was investigated in this paper. The results show that, under the same technology conditions, the thickness of hot-dipped aluminizing layer by adding the appropriate content of rare-earth La is about 2~3 times as much as that without rare-earth La, and the microstructure of hot-dipped aluminizing layer has also greatly changed ,and a great deal of phase Fe3Al was precipitated along the boundary of a phase. The corrosion resistance of the hot-dipped layer with rare-earth is greatly increased.
出处
《材料热处理学报》
EI
CAS
CSCD
北大核心
2004年第05B期1291-1294,共4页
Transactions of Materials and Heat Treatment
关键词
显微结构
耐蚀性
稀土
热浸
铝钢
rare-earth, aluminum, hot-dipped aluminum, corrosion