摘要
Mg-content cored-wire was used to desulphurize and spheroidize ductile iron melt in industrial experiments. The optimal feeding speed and suitable treatment temperature were determined in the experiments. And cored-wire method and pouring method were compared. Conclusions have been drawn that, under these conditions in the experiments, the optimal feeding speed is 15m/min, treatment temperature should be as low as possible, 1400-1450℃ generally; and cored-wire method can act more effective in ductile iron melt desulphurization and spheroid than pouring method.
Mg-content cored-wire was used to desulphurize and spheroidize ductile iron melt in industrial experiments. The optimal feeding speed and suitable treatment temperature were determined in the experiments. And cored-wire method and pouring method were compared. Conclusions have been drawn that, under these conditions in the experiments, the optimal feeding speed is 15m/min, treatment temperature should be as low as possible, 1400-1450℃ generally; and cored-wire method can act more effective in ductile iron melt desulphurization and spheroid than pouring method.
基金
the High Technology Research and Development Program of China(No.2002A4336072)