摘要
本文利用扫描电镜仔细观察了300M钢孔挤压强化后疲劳断口的形貌;研究了疲劳裂纹的起始与扩展特征;探讨了孔挤压强化明显推迟疲劳裂纹起始、降低疲劳裂纹扩展速率的机理。
atigue fracture of 300M steel after holes coining strenthening has been observed in detail by all means of SEM; The characteristic of fatigue crack initiation and propagation has been studied. The mecha-nism of defered initiation of crack and reduction of crack propagation rate owing to holes coining has been discussed also.